Ferrite Magnet
SinteredFerrite MagnetZvinhu Zvenyama | |||||||||
Giredhi | Remanence | Rev. Temp. Coeff. Kubva Br | Coercive Force | Intrinsic Coercive Force | Rev. Temp.-Coeff. Kubva Hcj | Max. Energy Product | Max. Operating Temperature | Density | |
Br (KGs) | Hcb (IWE) | Hcj (IWE) | (BH) max. (MGOe) | g/cm³ | |||||
Y10T | 2.0-2.35 | -0.20 | 1.57-2.01 | 2.64-3.52 | +0.30 | 0.8-1.2 | 250 ℃ | 4.95 | |
Y20 | 3.2-3.8 | -0.20 | 1.70-2.38 | 1.76-2.45 | +0.30 | 2.3-2.8 | 250 ℃ | 4.95 | |
Y22H | 3.1-3.6 | -0.20 | 2.77-3.14 | 3.52-4.02 | +0.30 | 2.5-3.2 | 250 ℃ | 4.95 | |
Y23 | 3.2-3.7 | -0.20 | 2.14-2.38 | 2.39-2.89 | +0.30 | 2.5-3.2 | 250 ℃ | 4.95 | |
Y25 | 3.6-4.0 | -0.20 | 1.70-2.14 | 1.76-2.51 | +0.30 | 2.8-3.5 | 250 ℃ | 4.95 | |
Y26H | 3.6-3.9 | -0.20 | 2.77-3.14 | 2.83-3.21 | +0.30 | 2.9-3.5 | 250 ℃ | 4.95 | |
Y27H | 3.7-4.0 | -0.20 | 2.58-3.14 | 2.64-3.21 | +0.30 | 3.1-3.7 | 250 ℃ | 4.95 | |
Y28 | 3.7-4.0 | -0.20 | 2.20-2.64 | 2.26-2.77 | +0.30 | 3.3-3.8 | 250 ℃ | 4.95 | |
Y30 | 3.7-4.0 | -0.20 | 2.20-2.64 | 2.64-2.77 | +0.30 | 3.3-3.8 | 250 ℃ | 4.95 | |
Y30H-1 | 3.8-4.0 | -0.20 | 2.89-3.46 | 2.95-3.65 | +0.30 | 3.4-4.1 | 250 ℃ | 4.95 | |
Y30BH | 3.8-3.9 | -0.20 | 2.80-2.95 | 2.90-3.08 | +0.30 | 3.4-3.7 | 250 ℃ | 4.95 | |
Y30-1 | 3.6-4.0 | -0.20 | 1.70-2.14 | 1.76-2.51 | +0.30 | 2.8-3.5 | 250 ℃ | 4.95 | |
Y30BH-1 | 3.8-4.0 | -0.20 | 2.89-3.46 | 2.95-3.65 | +0.30 | 3.4-4.0 | 250 ℃ | 4.95 | |
Y30H-2 | 3.95-4.15 | -0.20 | 3.46-3.77 | 3.90-4.21 | +0.30 | 3.5-4.0 | 250 ℃ | 4.95 | |
Y20-2 | 3.95-4.15 | -0.20 | 3.46-3.77 | 3.90-4.21 | +0.30 | 3.5-4.0 | 250 ℃ | 4.95 | |
Y32 | 4.0-4.2 | -0.20 | 2.01-2.38 | 2.07-2.45 | +0.30 | 3.8-4.2 | 250 ℃ | 4.95 | |
Y33 | 4.1-4.3 | -0.20 | 2.77-3.14 | 2.83-3.21 | +0.30 | 4.0-4.4 | 250 ℃ | 4.95 | |
Y35 | 4.0-4.1 | -0.20 | 2.20-2.45 | 2.26-2.51 | +0.30 | 3.8-4.0 | 250 ℃ | 4.95 | |
Cherechedza: · Isu tinoramba takafanana nepamusoro kunze kwekunge tadudzwa kubva kumutengi. Curie tembiricha uye tembiricha coefficient ndezvekutarisa chete, kwete sehwaro hwesarudzo.· Tembiricha yepamusoro yekushanda yemagineti inochinjika nekuda kwereshiyo yehurefu uye dhayamita nemamiriro ekunze. |
Advantage:
Sezvinongoita oxide ceramics, yakaoma ferrite magineti anoratidza hunhu husingaite kune hunyoro, zvinonyungudutsa, alkaline mhinduro,
maasidhi asina simba, munyu, mafuta ekuzora uye zvinosvibisa gasi. Kazhinji, magineti akaomeswa ferrite anogona saka kushandiswa pasina yekuwedzera corrosion dziviriro.
Feature:
Nekuda kwekuoma kwavo kukuru (6-7 Mohs), magineti eFerrite ane brittle uye anonzwa kugogodza kana kukotama. Panguva yekugadzirisa, dzinofanirwa kugadzirwa nemidziyo yedhaimondi. Matembiricha ekushanda ane magineti eferrite anowanzo ari pakati pe -40ºC ne250ºC.
Application:
Maumbirwo akasiyana anoshandiswa mune otomotive engineering, senge otomatiki uye kuyerwa kudzora. Zvimwe zvinoshandiswa zvakaita seMota yemagetsi muchina (wipers, sit chair mota), Kudzidzisa, Door absorber, Magnetic bhasikoro uye masaja chair, nezvimwe.
Nhasi, maferrite akaomarara anomiririra chikamu chikuru chemagetsi echigarire anogadzirwa. Kusiyana nemagineti eAlNiCo, maferrite akaomeswa anoratidzirwa nekudzikama densities asi yakakwirira yekumanikidza munda masimba. Izvi zvinoguma mune kazhinji flat chimiro chemidziyo. Barium ferrite uye strontium ferrite inosiyaniswa zvichienderana nekutanga zvinhu.
Ese maitiro akataurwa akatemerwa uchishandisa akajairwa masampuli zvinoenderana neIEC 60404-5. Zvinotevera zvinotsanangurwa zvinoshanda sereferenzi uye zvinogona kusiyana.